Experimental design of the bearing performances of flax fiber reinforced epoxy composites by a failure map
2018
Abstract This paper represents the first effort aimed to the investigation of the pin/hole contact stress and failure mechanisms of epoxy composites reinforced with woven flax fabrics, underwent to tensile bearing tests. In particular, the maximum loads and failure modes are evaluated at varying the laminate geometrical configuration. In order to optimize the use of polymer composites reinforced with flax fibers in structural applications, an experimental failure map, identifying main failure modes of mechanically fastened joints, is obtained as function of hole diameter, distance of the hole from the free edge of the laminate and laminate width. Moreover, a theoretical approach based on th…
Failure maps to assess bearing performances of glass composite laminates
2018
Aim of this article is the assessment of the bearing mechanical performances of pin-loaded glass laminates as function of their geometrical configuration. To this concern, 32 specimens having different hole diameter (D), laminate width (W), and hole center to laminate free edge distance (E) have been tested under bearing conditions. The maximum bearing stress and the stress-displacement curves were analyzed as function both of hole to laminate free edge distance E and hole diameter D. Moreover, an experimental 2D failure map was created by placing the experimental results (i.e., the kind of failure mechanism occurred for each geometrical configuration) in the plane E/D versus W/D ratios. In…
Bearing strength and failure behavior of pinned hybrid glass-flax composite laminates
2018
Abstract The aim of the present work is to evaluate the influence of external layers of glass woven fabric on the pin-hole strength of flax/epoxy laminates. Single lap bearing tests were carried out to evaluate the fastened joint performances depending on laminate stacking sequence. In order to better identify the mechanical behavior of the hybrid laminate, full glass and flax laminates were also compared. In particular, bearing stress and failure mechanisms were investigated at varying joint geometry. Furthermore, an experimental failure map, clustering main failure modes of pinned hybrid composite laminate, was used to better clarify the relationship between mechanical failure and geometr…
An aging evaluation of the bearing performances of glass fiber composite laminate in salt spray fog environment
2019
The aim of the present paper is to assess the bearing performance evolution of pinned, glass-composite laminates due to environmental aging in salt-spray fog tests. Glass fibers/epoxy pinned laminates were exposed for up to 60 days in salt-spraying, foggy environmental conditions (according to ASTM B117 standard). In order to evaluate the relationship between mechanical failure mode and joint stability over increasing aging time, different single lap joints, measured by the changing hole diameter (D), laminate width (W) and hole free edge distance (E), were characterized at varying aging steps. Based on this approach, the property-structure relationship of glass-fibers/epoxy laminates was a…
Evolution of the bearing failure map of pinned flax composite laminates aged in marine environment
2020
Abstract Aim of the present paper is to evaluate how the bearing behavior of pinned flax composites can be influenced by their exposition to critical environment such as marine one. To this scope, flax fibers/epoxy pinned laminate was exposed up to 60 days to salt-fog environment, according to ASTM B 117 standard. In particular, samples having different hole diameter (D), laminate width (W), and hole center to laminate free edge distance (E) have been tested under single lap bearing tests at varying the aging exposition time. Following this procedure, an experimental 2D failure map clustering main failure modes was created by placing the experimental results in the plane E/D versus W/D rati…